Glass bottle is not qualified to check how? Glass bottle production and manufacturing from the time out of the water bottle seat team machine workers first look at the approximate condition of the goods, and then according to a period of quenching, and workshop management in careful and careful, about the condition of the following categories.
Glass bottle is not qualified to check how
1. Glass bottle bottle body deformation
As the forming mold in the water bottle seat are not yet moon prana stereotypes, this time the temperature of the feed drops and influence the temperature is too high will often make the glass bottle step into deformation, assuming that the upper end of the bottle is too heavy will also be so. Sometimes the bottom of the bottle is not cooled to the inevitable temperature will be printed on the grain marks of the conveyor belt and thus the bottom of the bottle is stubborn.
2. Glass bottle body material path marks
Glass bottle manufacturers recommend that the channel marks are the most common problem of glass bottles. It can appear unusually fine, there are some only in the refracted light to create. Often caused by the location of the cork, short plate and shoulders, the bottle body and the bottom of the bottle also often appear material road marks, when the points due to the temperature of the melting furnace caused.
3. glass bottles of thin and thick disproportionate
Assuming that the glass bottle manufacturers in the production and processing process on the edge of the glass material drop temperature is not uniform, high temperature part of the viscosity is small, very easy to blow thin, low temperature part of the friction resistance, thick. Another mold shell temperature disproportionate, the high temperature side of the glass cooling slow, very easy to blow thin, low temperature side, because the glass cooling fast and blow thick.
4. The natural environment of glass bottle cracks
Crack has various appearance design, some are wrinkles, some are a piece of fine wrinkles, the main reason caused by the material drops low temperature, the material drops are too long, the material drops did not fall in the center of the initial mold management and adhesion in the inner wall of the core and caused.
5. Vapor bubble
Glass bottle manufacturers in the forming process caused by the side of the bubble is often more than one large bubble or concentrated in the number of bubbles, which is different from the glass itself is evenly distributed bubbles.